Indentation Strain Rate Sensitivity of CoCrFeNiAl0.3 High?Entropy Alloy

The strain rate sensitivity and indentation size effect of CoCrFeNiAl0.3 are investigated. Indentation strain rate has a negligible effect on the indentation contact stiffness and elastic modulus, whereas the hardness exhibits strain rate sensitivity. The strain rate sensitivity exponent free from the effect of indentation depth is obtained.In this paper, the mechanical properties of CoCrFeNiAl0.3 high?entropy alloy (HEA) under different strain rates are investigated using nanoindentation at room temperature. Experimental results show that the contact stiffness increases almost linearly with indentation depth and the elastic modulus is invariable under different indentation strain rates, while the indentation hardness under higher strain rate is relatively larger, and the hardness under large indentation depth is relatively smaller for each indentation strain rate. The indentation size effect of hardness and strain rate sensitivity exponent m under different indentation strain rates are analyzed, then the hardness and m free from the effect of indentation depth are obtained. Finally, this investigation reveals the size effects of the hardness of HEA in light of the strain rate sensitivity and activation volume of the dislocation nucleation.

» Author: Ji Qiu, Gesheng Xiao, Tao Jin, Buyun Su, Xuefeng Shu, Shengguo Ma

» Reference: doi:10.1002/adem.201800744

» Publication Date: 18/10/2018

» More Information

« Go to Technological Watch

LATEST NEWS TECHNOLOGICAL WATCH

[17/01/2019] - Global Brominated Flame Retardants Market Analysis & Outlook 2019-2023 - Dominant Players are AkzoNobel, Albemarle, ICL, Jiangsu Yoke Technology, LANXESS, and Velsicol Chemical - ResearchAndMarkets.com

[17/01/2019] - New Flame-retardant Structural Adhesive for Aircraft Interior Fabrication

[17/01/2019] - Report: Global injection molding machine market to grow at 3.5 percent

[17/01/2019] - Nanotech Energy, the UCLA Energy Incubator and Holder of First Patent for Graphene Announces Profound Achievement in Production of High Quality Graphene Based Materials

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n [310187].